ICON AS-4310

Media Finish: Gloss
Media Width: 54"
Roll Length: 45m (Full Roll)
Log in to purchase


ICON® AS-4310 is a 82 micron flexible white calendered vinyl film, backed with a pressure sensitive acrylic adhesive system, specifically engineered to adhere to a broad variety of surfaces. Suggested applications include LSE/HSE plastics, unfinished metal, wood, walls, corrugated paper, and other difficult to adhere to smooth surfaces.



Recommended Uses

Substance Incorporated recommends the following end uses for ICON® AS-4310: An economical choice for applications where standard films will not adhere. Graphics and wall murals applied to low VOC paints and mildly textured walls. Graphics and decals applied to smooth LSE/HSE plastics, or unfinished metal. Promotional decals where the end-use is undetermined, and adhesion is critical.



ICON® AS-4310
Material 82 micron Calendered Vinyl
Colour White
Tensile Strength 63N/25mm
Adhesive Clear Solvent-Based Pressure Sensitive Acrylic
Adhesive Thickness 0.02mm +/-10%
Peel Adhesion 22.7N/25mm from Stainless Steel
Liner 93LB PE Coated Layflat Paper
Liner Release 30 grams/25mm
Dimensional Stability 1.0 mm
Application Temp. 0°C to 27°C recommended, test prior to specific application
Temperature Range -53°C to 100°C
Shelf Life 2 years when stored at 21°C and 50% relative humidity
Print Compatability Solvent, Eco-Solvent, Latex, UV, and Thermal Transfer Inks
Graphic Life Outdoor durability up to 5 years (unprinted), permanent
Chemical Resistence Resists mild acids, mild akalis, solvents, and salts. Excellent resistance to water, including immersion.



Before applying an overlaminate, allow 24-48 hours for print to dry. Application surface must be free of dust, dirt, debris, grease, and other contaminants. We highly recommend cleaning the installation surface with isopropyl alcohol prior to application. Dry installation is recommended. Due to a highly-aggressive adhesive system, AS-4310 will exhibit a slightly higher amount of shrinkage than standard calendered vinyl films.